Fiberglass Chopped Strand Needle Mat 560 gsm
The fiberglass needled mat is a kind of material which is the fiberglass crossing the space without orders.
Fiberglass Needle Mat Series:
Model No. | Weight | Width | Net Weight per Roll | |||
(oz. per sq/ft) | (grams per sq/m) | (inch) | (mm) | (lb) | (kg) | |
EMNC | 0.98-3 | 300-910 | 32-41 | 820-1050 | 88-110 | 40-50 |
Use And Craftwork: GMT | ||||||
EMNS | 0.98-3 | 300-910 | 32-41 | 820-1050 | 88-110 | 40-50 |
Use And Craftwork: GMT | ||||||
EMNS-P | 1.47-2.5 | 450-760 | 36-41 | 910-1050 | 55-66 | 25-30 |
Use And Craftwork: Pultrusion |
Capabilities:
1. Three-dimensional structure
2. Needled by the chopped strand or continuous strand
3. It will be porous structure when heated. The structure avoids the defects caused by the air embedded into the products.
4. Evenly distribution makes sure the Smoothness of the finished.
5. High tensile strength greatly increases the mechanical capability of the products.
Application:
Fiberglass composite mat has the characteristics of both continuous filament mats and chopped strand mats, which are flowing faster in layer resin and also with faster and well wet-out rate. Continuous/polyester veil composite mat has higher strength and more clear surface. These two kind mat are widely used in Pultrusion, RTM and also high requirements molding process.
Packaging:
Packed by rolls.
Storage:
Unless otherwise specified, fiberglass products should be stored in a dry, cool and moistureproof area. Room temperature and humidity should always be maintained at 15°C – 35°C, 35% – 65% respectively. Best used within 12 months after production date. Fiberglass products should remain in their original packaging until just prior to use.
Fiberglass Chopped Strand Needle Mat 560 gsm
The fiberglass needled mat is a kind of material which is the fiberglass crossing the space without orders.
Fiberglass Needle Mat Series:
Model No. | Weight | Width | Net Weight per Roll | |||
(oz. per sq/ft) | (grams per sq/m) | (inch) | (mm) | (lb) | (kg) | |
EMNC | 0.98-3 | 300-910 | 32-41 | 820-1050 | 88-110 | 40-50 |
Use And Craftwork: GMT | ||||||
EMNS | 0.98-3 | 300-910 | 32-41 | 820-1050 | 88-110 | 40-50 |
Use And Craftwork: GMT | ||||||
EMNS-P | 1.47-2.5 | 450-760 | 36-41 | 910-1050 | 55-66 | 25-30 |
Use And Craftwork: Pultrusion |
Capabilities:
1. Three-dimensional structure
2. Needled by the chopped strand or continuous strand
3. It will be porous structure when heated. The structure avoids the defects caused by the air embedded into the products.
4. Evenly distribution makes sure the Smoothness of the finished.
5. High tensile strength greatly increases the mechanical capability of the products.
Application:
Fiberglass composite mat has the characteristics of both continuous filament mats and chopped strand mats, which are flowing faster in layer resin and also with faster and well wet-out rate. Continuous/polyester veil composite mat has higher strength and more clear surface. These two kind mat are widely used in Pultrusion, RTM and also high requirements molding process.
Packaging:
Packed by rolls.
Storage:
Unless otherwise specified, fiberglass products should be stored in a dry, cool and moistureproof area. Room temperature and humidity should always be maintained at 15°C – 35°C, 35% – 65% respectively. Best used within 12 months after production date. Fiberglass products should remain in their original packaging until just prior to use.